Effect of fibre orientation on the low velocity impact response of thin Dyneema® composite laminates

Research output: Contribution to journalArticle

Original languageEnglish
Pages (from-to)35-45
Number of pages11
JournalInternational Journal of Impact Engineering
Early online date28 Oct 2016
DateAccepted/In press - 25 Oct 2016
DateE-pub ahead of print - 28 Oct 2016
DatePublished (current) - 1 Feb 2017


Ultra-high molecular weight polyethylene (UHMWPE) fibre reinforced composite materials are widely used in ballistic impact and collision scenarios due to their extremely high specific strength and stiffness. Exceptional levels of protection are provided by controlling the damage and deformation mechanisms over several length scales. In this study, the role of UHMWPE fibre architecture (cross-ply, quasi-isotropic and rotational “helicoidal” layups) is considered on the damage and deformation mechanisms arising from low velocity impacts with 150 J impact energy and clamped boundary conditions. Dyneema® panels approximately 2.2 mm thick were impacted with a fully instrumented hemi-spherical impactor at velocities of 3.38 m/s. Full field deformation of the panels was captured through digital image correlation (DIC). The results indicate that the cross-ply laminate [0°/90°] had the largest back face deflection, whilst quasi-isotropic architectures restricted and reduced the central deflection by an average of 43%. In the case of the [0°/90°] panel, the deformation mechanisms were dominated by large amounts of in-plane shear with limited load transfer from primary fibres. Conversely, the failure of the quasi-isotropic panels were dominated by large amounts of panel buckling over various length scales. The observed mechanisms of deformation with increasing length scale were; through thickness fibre compression, fibre micro-buckling, fibre re-orientation with large matrix deformation, lamina kink band formation, and laminate buckling. The helicoidal panels showed that bend-twist and extension-twist coupling were important factors in controlling clamped boundary conditions and the laminate buckling/wrinkling shape. Further examination of the impact zone indicated that the damage mechanisms appear to be fibre orientation dependent, with quasi-isotropic laminates having up to 37.5% smaller impact damage zones compared with [0°/90°]. The experimental observations highlight the importance of fibre orientation in controlling the deformation mechanisms under dynamic impact, in particular limiting the shear deformation of Dyneema® panels.

    Research areas

  • Digital image Correlation, Drop weight, Dyneema, Impact

Download statistics

No data available



  • Full-text PDF (accepted author manuscript)

    Rights statement: This is the author accepted manuscript (AAM). The final published version (version of record) is available online via Elsevier at Please refer to any applicable terms of use of the publisher.

    Accepted author manuscript, 8 MB, PDF-document

    Licence: CC BY-NC-ND


View research connections

Related faculties, schools or groups